dc.contributor.authorБойко, А. А.
dc.contributor.authorЗализный, Д. И.
dc.contributor.authorАль-Камали, М. Ф. С. Х.
dc.contributor.authorПодденежный, Е. Н.
dc.contributor.authorАлексеенко, Ю. А.
dc.contributor.authorДробышевская, Н. Е.
dc.contributor.authorАль-Арики, Н. A. С.
dc.contributor.authorГолосов, Д. А.
dc.contributor.authorДоан, Х. Т.
dc.coverage.spatialГомельru_RU
dc.date.accessioned2022-10-04T13:48:17Z
dc.date.available2022-10-04T13:48:17Z
dc.date.issued2022
dc.identifier.citationВлияние тонкопленочных покрытий SiO2 : Me на эффективность фотогенерирующих элементов / А. А. Бойко [и др.] // Вестник ГГТУ им. П. О. Сухого : научно-практический журнал. — 2022. — № 3. — С. 44—54.ru_RU
dc.identifier.urihttps://elib.gstu.by/handle/220612/26673
dc.description.abstractПредставлены результаты исследований влияния тонкопленочных покрытий на основе SiO2 : Cux и SiO2 : Nix на КПД фотоэлементов (использовались фотоэлементы Aoshike). Отработаны технологические режимы получения мишеней, содержащих наночастицы ионов переходных металлов, и определены режимы нанесения тонких пленок на подложки методом импульсного лазерного испарения. Результаты исследований вольт-амперных характеристик показали, что покрытия с применением никеля, а также покрытия с минимальной концентрацией меди являются наилучшими. Эффективность фотоэлементов с этими покрытиями практически такая же, как у чистых образцов. Значения Pmax у них даже несколько выше, однако о явном увеличении КПД говорить преждевременно, так как полученные отклонения Pmax находятся в рамках погрешности измерений и разброса параметров покрытий.ru_RU
dc.description.abstractThe results of studies of the influence of thin film coatings based on SiO2 : Cux and SiO2 : Nix on the efficiency of photocells (Aoshike photocells were used) are presented. Technological modes of obtaining targets containing nanoparticles of transition metal ions were worked out, and modes of applying thin films to substrates were deter mined by pulse laser evaporation. The results of studies of voltage-ampere characteristics showed that coatings using nickel, as well as coatings with a minimum copper concentration, are the best. The efficiency of photocells with these coatings is practically the same as that of pure samples. They have even slightly higher Pmax values, but it is premature to talk about a clear increase in efficiency, since the resulting Pmax deviations are within the measurement error and spread of coating parameters.
dc.language.isoruru_RU
dc.publisherГГТУ им. П.О. Сухогоru_RU
dc.subjectТонкие пленкиru_RU
dc.subjectИоны медиru_RU
dc.subjectИоны никеляru_RU
dc.subjectФотоэлементru_RU
dc.subjectВольт-амперная характеристикаru_RU
dc.subjectПоследовательное сопротивлениеru_RU
dc.subjectКПДru_RU
dc.subjectThin filmsru_RU
dc.subjectCopper ionsru_RU
dc.subjectNickel ionsru_RU
dc.subjectPhotocellru_RU
dc.subjectVoltage-ampere characteristicru_RU
dc.subjectSerial resistanceru_RU
dc.subjectEfficiencyru_RU
dc.titleВлияние тонкопленочных покрытий SiO2 : Me на эффективность фотогенерирующих элементовru_RU
dc.title.alternativeInfluence of SiO2 Thin Film Coatings : Meon Efficiency of Photogenerating Elementsru_RU
dc.typeArticleru_RU
dc.identifier.udc621.311.001.57